Cobalt Chrome Compositions for Dental Laboratory. Non-precious alloy for metal - ceramic work or composite veneering. We have two kinds of Co-Cr dental ceramic alloy compositions. These compositions according to our customer demand and the long years of research produced by our company. When you ordering specify what is a soft metal or hard metal
Diameter : 8 mm X 17 mm
Packing: 1 kg Plastic / Wood Box,
Carton Box, Leather Packing
No Nickel - No Berylium
Melting Range: 1350-1400°C
Ductile Yield (A5): %6
Elongation: 390(MPa)
Vickers Hardness: 360
Density: 8.5 (g/cm)
Modulus of Elasticity: 210,000 (MPa)
Denture Alloy: Cobalt Chrome Compositions for Dental Laboratory. We have a kind of CAST-CC partial denture alloy composition. These compositions according to our customer demand and the long years of research produced by our company.
Diameter : 8 mm X 20 mm
Packing: 1 kg Plastic / Wood Box,
Carton Box, Leather Packing
Melting Range: 1350-13800°C
Ductile Yield (A5): %7.5
Tensile Strenght: 970(MPa)
Elongation: 670(MPa)
Vickers Hardness: 400
Density: 8.3 (g/cm)
Modulus of Elasticity: 220,000 (MPa)
Tensile Streght (RM): 910
Denture Alloy: Cobalt Chrome Compositions for Dental Laboratory. We have a kind of CAST-CC partial denture alloy composition. These compositions according to our customer demand and the long years of research produced by our company.
Shape : Shot Form
Packing: 1 kg Plastic / Wood Box,
Carton Box, Leather Packing
Melting Range: 1350-13800°C
Ductile Yield (A5): %7.5
Tensile Strenght: 970(MPa)
Elongation: 670(MPa)
Vickers Hardness: 400
Density: 8.3 (g/cm)
Modulus of Elasticity: 220,000 (MPa)
Tensile Streght (RM): 910
Nickel Chrome Compositions for Dental Laboratory. Non-precious alloy for metal - ceramic work or composite veneering. We have two kinds of Ni-Cr dental ceramic alloy compositions. These compositions according to our customer demand and the long years of research produced by our company. When you ordering specify what is a soft metal or hard metal
Diameter : 8 mm X 15 mm
Packing: 1 kg Plastic / Wood Box,
Carton Box, Leather Packing
No Berylium
Melting Range: 1200-1250°C
Ductile Yield (A5): %25
Elongation: 330(MPa)
Vickers Hardness: 220
Density: 8.2 (g/cm)
Modulus of Elasticity: 205,000 (MPa)
Nickel Chrome Compositions for Dental Laboratory. Non-precious alloy for metal - ceramic work or composite veneering. We have two kinds of Ni-Cr dental ceramic alloy compositions. These compositions according to our customer demand and the long years of research produced by our company. When you ordering specify what is a soft metal or hard metal
Diameter : 8 mm X 15 mm
Packing: 1 kg Plastic / Wood Box,
Carton Box, Leather Packing
No Berylium
Melting Range: 1200-1250°C
Ductile Yield (A5): %25
Elongation: 330(MPa)
Vickers Hardness: 220
Density: 8.2 (g/cm)
Modulus of Elasticity: 205,000 (MPa)
Nickel Chrome Soldering for Dental Laboratory. Non-precious alloy for metal - ceramic work or composite veneering. We have a kinds of Ni-Cr dental soldering. These soldering according to our customer demand and the long years of research produced by our company.
Diameter : 1 mm
Packing: 1 Glass box
Weight: 30 gr
No Berylium
Melting Range: 1150-1250°C
Ductile Yield (A5): %25
Elongation: 330(MPa)
Vickers Hardness: 220
Density: 8.2 (g/cm)
Modulus of Elasticity: 205,000 (MPa)
Cobalt Chrome Dental alloy Blank - For Cad Cam Dental ceramic. TS EN ISO 22674:2007 EN ISO: 9001-2009 Standarts. These compositions according to our customer demand and the long years of research produced by our company. When ordering sepcify which dimensions to below. The most recent for instruction and chemical compositions. Can be obtained from our company.
Diameter: 98Ø x 8, 10, 12, 14, 16, 18, 20 mm
Melting Range: 1350-1400°C
Ductile Yield (A5): %6
Elongation: 390(MPa)
Vickers Hardness: 360
Density: 8.5 (g/cm)
Modulus of Elasticity: 210,000 (MPa)
Coefficient of the liner expansion: 14-14,2 x10-6 K-1
Easy production, Light metal protesis, Fast milling, Exellent connective tissue, Hardness, Surface quality, Minimum oxidation, Excellent porcelain compliance, Equal thickness at every point, No balance, No Berylium
Nickel Chrome Dental alloy Blank - For Cad Cam Dental ceramic. TS EN ISO 22674:2007 EN ISO: 9001-2009 Standarts. These compositions according to our customer demand and the long years of research produced by our company. When ordering sepcify which dimensions to below. The most recent for instruction and chemical compositions. Can be obtained from our company.
Diameter: 98Ø x 8, 10, 12, 14, 16, 18, 20 mm
Melting Range: 1200-1250°C
Ductile Yield (A5): %25
Elongation: 330(MPa)
Vickers Hardness: 220
Density: 8.2 (g/cm)
Modulus of Elasticity: 205,000 (MPa)
Coefficient of the liner expansion: 14-14,2 x10-6 K-1
Easy production, Light metal protesis, Fast milling, Exellent connective tissue, Hardness, Surface quality, Minimum oxidation, Excellent porcelain compliance, Equal thickness at every point, No balance, No Berylium
Induction casting machine producing companies in the world in different forms appropriate Crucibles manufactures its own machines. However, the new form from you in the future Crucibles can be produced. Crucibles Alumina, SC is manufactured using high temperature and shock resistant. Still needs to be baked in the oven headlines. This process will definitely extend the life of the crucible. Our standart 2-form produced crucibles can be manufactured according to demmands from you the future.
%100 Extra White Ceramic
Packing: 12 Pcs / Box
Induction casting machine producing companies in the world in different forms appropriate Crucibles manufactures its own machines. However, the new form from you in the future Crucibles can be produced. Crucibles Alumina, SC is manufactured using high temperature and shock resistant. Still needs to be baked in the oven headlines. This process will definitely extend the life of the crucible. Our standart 2-form produced crucibles can be manufactured according to demmands from you the future.
%100 Extra White Ceramic
Packing: 12 Pcs / Box
The world known as high temparature and shock resistant Alumina, silicon carbur is produced. Deformation without cracking a long time before you can use. Crucibles not stick to metal. Shock resistant. How ever, along with casting before heading for extended periods of crucible to oven is very useful. Crucibles can be produced in different forms according to your request.
100% Extra White Ceramic Elextomelt
Packing: 12 Pcs / Box
The world known as high temparature and shock resistant Alumina, silicon carbur is produced. Deformation without cracking a long time before you can use. Crucibles not stick to metal. Shock resistant. How ever, along with casting before heading for extended periods of crucible to oven is very useful. Crucibles can be produced in different forms according to your request.
100% Extra White Ceramic Elextomelt
Packing: 12 Pcs / Box
The world known as high temparature and shock resistant Alumina, silicon carbur is produced. Deformation without cracking a long time before you can use. Crucibles not stick to metal. Shock resistant. How ever, along with casting before heading for extended periods of crucible to oven is very useful. Crucibles can be produced in different forms according to your request.
100% Extra White Ceramic Elextomelt
Packing: 12 Pcs / Box
The world known as high temparature and shock resistant Alumina, silicon carbur is produced. Deformation without cracking a long time before you can use. Crucibles not stick to metal. Shock resistant. How ever, along with sintering before heading for extended periods of crucible to oven is very useful. Crucibles can be produced in different forms according to your request.
100% Extra White Ceramic Elextomelt
Packing: 1 Pcs / Wooden Box
The world known as high temparature and shock resistant Alumina, silicon carbur is produced. Deformation without cracking a long time before you can use. Crucibles not stick to metal. Shock resistant. How ever, along with sintering before heading for extended periods of crucible to oven is very useful. Crucibles can be produced in different forms according to your request.
100% Extra White Ceramic Elextomelt
Packing: 1 Pcs / Wooden Box
The world known as high temparature and shock resistant Alumina, silicon carbur is produced. Deformation without cracking a long time before you can use. Sinter ball not stick to metal. Shock resistant. How ever, along with sintering before heading for extended periods of sinter ball to oven is very useful. Sinter ball can be produced in different forms according to your request.
100% Extra White Ceramic Elextomelt
Packing: 400 gr / Plastic Box
Turkey's first and only domestically produced separating disc. It is the world's best quality and long-lasting separating disc.
It allows you to produce your work with maximum quality without slowing down where fine workmanship is required.
The number one choice of dental technicians in the world.
Speedy cutting maximum performace.
Reinforced Fiber Glass
Dimension: 38Ø x 1.0 mm
Packing: 50 pcs / Box
For all type Alloys.
Turkey's first and only domestically produced separating disc. It is the world's best quality and long-lasting separating disc.
It allows you to produce your work with maximum quality without slowing down where fine workmanship is required.
The number one choice of dental technicians in the world.
Speedy cutting maximum performace.
Dimension: 38Ø x 0.7 - 1.0 - 1.7 mm
Packing: 50 pcs / Box
For all type Alloys.
The Alloy melting process is used to manufacture dental products such as crowns, bridges, model castings and secondary structures in economical. High-quality, Wonderful fitting dentures made of nickel chromium, cobalt chromium, titanium or precious - metal alloys
Material Dental Sintered Powder
Tensile Strenght: 480-520 (MPa)
Elongation: 10-15 (%)
Hardness: 220-250 HV0.1
Surface finish: (µm) Rz 30-60
Accuracy: ±0.1 (mm)
Density: ca. 100%
Excellent connective, Hardness, Surface quality, Minimum oxidation, Excellent porcelain compliance. No balance, No risk of allergy, No berylium.No Nickel, Best Laser Sintering Powder
The Alloy melting process is used to manufacture dental products such as crowns, bridges, model castings and secondary structures in economical. High-quality, Wonderful fitting dentures made of nickel chromium, cobalt chromium, titanium or precious - metal alloys
Material Dental Sintered Powder
Tensile Strenght: 480-520 (MPa)
Elongation: 10-15 (%)
Hardness: 220-250 HV0.1
Surface finish: (µm) Rz 30-60
Accuracy: ±0.1 (mm)
Density: ca. 100%
Excellent connective, Hardness, Surface quality, Minimum oxidation, Excellent porcelain compliance. No balance, No risk of allergy, No berylium. Best Laser Sintering Powder